Physical Properties物理性质

Metric公制数据

English英制数据

Comments测试方法

Specific Gravity比重 

1.28 g/cc

1.28 g/cc

ASTM D792

Water Absorption吸水率 

0.20 %
@Temperature 23.0 °C

0.20 %
@Temperature 73.4 °F

Equilibrium 50%RH; ISO 62

0.30 %
@Temperature 23.0 °C

0.30 %
@Temperature 73.4 °F

Immersion 24h; ASTM D570

0.30 %
@Temperature 23.0 °C

0.30 %
@Temperature 73.4 °F

Immersion 24h; ISO 62

0.60 %
@Temperature 23.0 °C

0.60 %
@Temperature 73.4 °F

Saturation, immersed; ISO 62

Linear Mold Shrinkage线性收缩率 

0.016 cm/cm

0.016 in/in

Flow; ASTM D955

Linear Mold Shrinkage, Flow线性收缩率/流动 

0.016 cm/cm
@Thickness 2.00 mm

0.016 in/in
@Thickness 0.0787 in

Parallel; ISO 294-4

Linear Mold Shrinkage, Transverse线性收缩率/横向 

0.016 cm/cm
@Thickness 2.00 mm

0.016 in/in
@Thickness 0.0787 in

Normal; ISO 294-4

Melt Flow熔体流动速率 

12.5 g/10 min
@Load 2.16 kg,
Temperature 240 °C

12.5 g/10 min
@Load 4.76 lb,
Temperature 464 °F

ASTM D1238

12.5 g/10 min
@Load 2.16 kg,
Temperature 240 °C

12.5 g/10 min
@Load 4.76 lb,
Temperature 464 °F

ISO 1133

Melt Index of Compound熔体流动速率 

10 g/10 min
@Load 2.16 kg,
Temperature 240 °C

10 g/10 min
@Load 4.76 lb,
Temperature 464 °F

cm3/10 min; ISO 1133

Mechanical Properties力学性能

Metric公制数据

English英制数据

Comments测试方法

Hardness, Shore D肖氏硬度D 

<= 82

<= 82

ASTM D2240

<= 82

<= 82

ISO 868

74
@Time 15.0 sec

74
@Time 0.00417 hour

ISO 868

Tensile Strength at Break断裂拉伸强度  

48.3 MPa
@Temperature 23.0 °C

7010 psi
@Temperature 73.4 °F

ASTM D638

50.0 MPa
@Temperature 23.0 °C

7250 psi
@Temperature 73.4 °F

ISO 527 (1BA bar)

Tensile Stress拉伸应力 

0.000 MPa
@Strain 0.000 %,
Temperature -40.0 °C

0.000 psi
@Strain 0.000 %,
Temperature -40.0 °F

ISO 527

9.71 MPa
@Strain 7.30 %,
Temperature 120 °C

1410 psi
@Strain 7.30 %,
Temperature 248 °F

ISO 527

19.62 MPa
@Strain 21.08 %,
Temperature 60.0 °C

2846 psi
@Strain 21.08 %,
Temperature 140 °F

ISO 527